ASTM B364-96(2002) (R1996)

1.1 This specification covers unalloyed and alloyed tantalum ingots prepared by vacuum-arc melting, electron-beam melting, or powder-metallurgy consolidation to produce consolidated metal for processing to various mill shapes.

1.2 The materials covered by this specification are:

1.2.1 R05200, unalloyed tantalum, electron-beam furnace or vacuum-arc melt, or both,

1.2.2 R05400, unalloyed tantalum, powder-metallurgy consolidation,

1.2.3 R05255, tantalum alloy, 90 % tantalum 10 % tungsten, electron-beam furnace or vacuum-arc melt, or both,

1.2.4 R05252, tantalum alloy, 97.5 % tantalum 2.5 % tungsten, electron-beam furnace or vacuum-arc melt, or both, and,

1.2.5 R05240 tantalum alloy, 60 % tantalum 40 % columbium, electron-beam furnace or vacuum-arc melt, or both.

1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.

This specification covers unalloyed and alloyed tantalum ingots prepared by vacuum-arc melting, electron-beam melting, or powder-metallurgy consolidation to produce consolidated metal for processing to various mill shapes. The materials covered by this specification are classified according to types: R05200; R05400; R05255; R05252; and R05240. The ingot metal for types R05200, R05255, R05252, and R05240 may be prepared by vacuum-arc melting, electron beam furnace melting, or a combination of these two methods. The metal for type R05400 is defined as powder-metallurgy consolidation unalloyed tantalum. The material shall conform to the chemical composition requirements for carbon, oxygen, nitrogen, hydrogen, niobium, iron, titanium, tungsten, molybdenum, silicon, nickel, and tantalum.